PROTEQ™ C4K2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SNpO0h_PROTEQ-C4K2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C4K2 is a medium flow, flame retardant grade of Polypropylene copolymer which meets the stringent UL94 V-2 and AS/NZS 60695.2.12 (IEC 60695-2-12) 960°C Glow Wire flammability test. Typical applications: Electrical appliances where a high level of flame retardancy is required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 180 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1100 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 30.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 180 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | > 850 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 28.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 100 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® TP10 | Toray Resin Company | ABS | Toyolac® |
| Aropol™ MR 14027 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Fainplast PVC CKL 90/40 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Dynalloy™ GP 7820-60N | PolyOne Corporation | TPE | Dynalloy™ |
| LNP™ LUBRICOMP™ Lexan_WR5210R compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |