Lupol® HG3200SK2
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SMrIHT_Lupol-HG3200SK2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Gloss Application Electrical & Electronic Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.4 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 34.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 20 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1960 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 44.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 3.20 mm) | 125 | °C | ASTM D648 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 4.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4135 | MBA Polymers | ABS | MBA ABS |
| RTP 300 SI 4 | RTP Company | PC | RTP |
| Boltaron 9815 | Boltaron Performance Products | PMMA+PVC | Boltaron |
| DINALON® B1S25 B30 | Grupo Repol | Nylon 6 | DINALON® |
| Elastollan® 585 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |