Lastilac SP G/17
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lastilac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SLyUkz_Lastilac-SP-G-17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Glass fibres. Product UL certified. High dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 to 0.65 | % | |
| Flow : 2.00 mm | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 5800 | MPa | |
| 60°C | 5300 | MPa | |
| 90°C | 4100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 75.0 | MPa | |
| Break, 60°C | 60.0 | MPa | |
| Break, 90°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.9 | % | |
| Break, 60°C | 3.3 | % | |
| Break, 90°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 75.0 | °C | |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 MS 2 | RTP Company | Nylon 66 | RTP |
| Prime Impax 450 with VANISH | Primex Plastics Corporation | PS (GPPS) | Prime Impax |
| TPV Elastoprene® N80A-i | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| PELPRENE™ P55U | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| POLYfill PPH TS15030 D | Polykemi AB | PP Homopolymer | POLYfill |