Hostacom M2 N42 L356015
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SLxGgF_HostacomM2N42L356015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom M2 N42 L356015 is a mineral filled PP homopolymer, with low melt flow rate. Product is UL listed. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 3100 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 68.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ HC MT222 | PolyOne Corporation | TPE | Versaflex™ |
| Nylene® 9110 G33 | Custom Resins Group | Nylon 610 | Nylene® |
| DOMAMID® 6ST2 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Elastron® G G500.A45.N.PS | Elastron USA, Inc. | SEBS | Elastron® G |
| KPOL-PP K-PPR 28.0 | KPOL Chem Co. | PP Random Copolymer | KPOL-PP |