| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Ensinger Inc. |
| Trademark: | TECASON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SKn05y_TECASON-P-MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECASON® P MT is a polyphenylsulfone suited primarily to applications in the medical industry. It is in the same performance category as products like Polysulfone and ULTEM® polyetherimide. TECASON® P MT has improved performance in terms of temperature, impact strength and chemical resistance. TECASON® P MT also has exceptional resistance to repeated steam autoclaving without loss of dimensional stability or physical properties. TECASON® PMT is available in several colored and transparent grades, as well as with our x-ray opaque XRO additive which allows for clear component visibility on fluorscopy and x-ray. TECASON® P MT series products are targeted at a number of applications in the medical industry.TECASON® P MT is often used in applications for surgical tools and instruments because of its resistance to autoclave sterilization damage. A second market for TECASON®, it is also a popular material choice for trials used in joint replacement surgeries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.37 | % | ASTM D570 |
| Saturated, 23°C | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2340 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 69.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2410 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 91.0 | MPa | ASTM D790 |
| Compressive Strength | 98.9 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 214 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 207 | °C | ASTM D648 |
| Vicat Softening Temperature | 218 | °C | |
| CLTE - Flow (-40 to 38°C) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1130 | J/kg/°C | ASTM C351 |
| Maximum Service Temperature - Intermittent | 182 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Dielectric Constant 1(23°C, 60 Hz) | 3.44 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Data obtained from injection molded samples. |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santron IMS1000M | Bhansali Engineering Polymers Limited | SAN | Santron |
| WEVO-CHEMIE Polyurethanes PU 304/300 | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| ACCUTECH™ NY0730G20L | ACLO Compounders Inc. | Nylon 6 | ACCUTECH™ |
| COSMOLEX® FS253R | TPC, The Polyolefin Company (Singapore) Pte Ltd | LLDPE | COSMOLEX® |
| LNP™ COLORCOMP™ 203RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |