LNP™ LUBRICOMP™ ZI001 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SIRqhB_LNP-LUBRICOMP-ZI001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZI001 is a compound based on PPE+PS resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound ZI001 Product reorder name: ZI001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 0.90 to 1.1 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2510 | MPa | ASTM D638 |
| -- | 2410 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 44.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/5 |
| Break 3 | 51.6 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.7 | % | ASTM D638 |
| Yield | 2.4 | % | ISO 527-2/5 |
| Break 5 | 36 | % | ASTM D638 |
| Break | 45 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2520 | MPa | ASTM D790 |
| -- 7 | 2390 | MPa | ISO 178 |
| Flexural Stress | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 9 | 140 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 118 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C EF750 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| NEFTEKHIM PE 4050Q (50403) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| DURACON® LU-02LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Sylvin 3290-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ WCD835 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |