Sindustris PC GP5057F
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SI80p7_Sindustris-PC-GP5057F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC GP5057F is a Polycarbonate + ABS (PC+ABS) material filled with 5.0% glass fiber. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC GP5057F are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.35 to 0.55 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 70.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3330 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 110 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 235 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.600 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J106G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| SABIC® LLDPE 430BE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| YUCLAIR® MM810 | SK Global Chemical | HDPE | YUCLAIR® |
| Exelene® PP C0800 | Montachem International, Inc. | PP Impact Copolymer | Exelene® PP |
| ELASTOSIL® E 43 | Wacker Chemie AG | Silicone | ELASTOSIL® E |