GETILAN GPE/400
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SHWC7A_GETILAN-GPE-400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable polythene. GETILAN GPE/400: medium density chemically crosslinkable compound for low voltage power cables insulation and sheathing. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our type MAC/100 SCU or MAC/202 less in reaction speed. REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 Certify: IEC 60502-1 XLPE, EPR/HEPR,CEI 2011 G7,HD 22-1 EI7 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 550 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811 | ||
| 127°C, 40 hr 1 | -9.0 | % | IEC 60811 |
| 150°C, 168 hr | -5.0 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air | IEC 60811 | ||
| 127°C, 40 hr | -5.0 | % | IEC 60811 |
| 150°C, 168 hr | -17 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 2(250°C) | 80 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | BS 6622 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 185 | °C | |
| Cylinder Zone 3 Temp. | 195 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C | |
| Die Temperature | 225 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for some hours (up to 3 mm thickness). Steam treatment at 0.15 for bar 5/6 hours. Faster ambient curing is possible depending from the atmospheric conditions. |
| Note Message | |
|---|---|
| 1 . | Air Bomb |
| 2 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® PC/PBT 3015 | Plastic Solutions, Inc. | PC+PBT | PrimaFlex® |
| YUPLENE® H230P | SK Global Chemical | PP Homopolymer | YUPLENE® |
| Hanwha Total PP GH42M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| INLUBE PPSCF30TF15 | Infinity LTL Engineered Compounds | PPS | INLUBE |
| Karina BLACK PVC COMPOUND 853-48/1-DY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |