TROGAMID® T BX7304
| Category: | Nylon 6/3T , Polyamide 6/3T Copolymer |
| Manufacturer: | Evonik Industries AG |
| Trademark: | TROGAMID® T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SH7GQI_TROGAMID-T-BX7304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp. In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles. TROGAMID® BX7304 Permanently transparent polymer blend consisting of an amorphous and semi-crystalline polyamide for injection molding; improved stress-cracking resistance, low water absorption. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.08 | g/cm³ | ISO 1183 |
| Viscosity Number | 160 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 84 | ISO 868 | |
| Ball Indentation Hardness | 130 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2200 | MPa | |
| 1000 hr | 800 | MPa | |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 8.0 | kJ/m² | |
| 23°C, Complete Break | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 93.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 99.0 | °C | ISO 306/B |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C, 1 MHz) | 0.043 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- 2 | 575 | V | |
| Solution A | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 930 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120CR | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| VITAMIDE® AY15BK6685 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| TOTAL Polystyrene Impact 945E | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| PlexTuf L-66119 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | PlexTuf |
| POCAN® B 3233 HR 000000 | LANXESS GmbH | PBT | POCAN® |