Monprene® IN-15056
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SFs9tY_Monprene-IN-15056.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene IN-15056 is a thermoplastic elastomer designed for the industrial market. Monprene IN-15056 exhibits low compression set, good abrasion and chemical resistance, and is suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 65 | ASTM D2240 | |
| Shaw A, 5 seconds | 63 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 2.34 | MPa | ASTM D412 |
| 200% strain | 3.06 | MPa | ASTM D412 |
| 300% strain | 3.97 | MPa | ASTM D412 |
| Tensile Strength (Break) | 14.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 730 | % | ASTM D412 |
| Tear Strength 1 | ASTM D624 | ||
| Transverse flow : 23°C | 33.0 | kN/m | ASTM D624 |
| Flow : 23°C | 33.7 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 11 | % | ASTM D395 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 35.0 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 232 | °C | |
| Cylinder Zone 2 Temp. | 188 - 238 | °C | |
| Cylinder Zone 3 Temp. | 193 - 243 | °C | |
| Cylinder Zone 5 Temp. | 199 - 249 | °C | |
| Die Temperature | 199 - 249 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | C mold, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 85A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| RTP EMI 261 A | RTP Company | Nylon 6 | RTP |
| VAMPTER C 0023 V0 | Vamp Tech | PC+PBT | VAMPTER |
| MAJORIS ET360 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| SEQUEL® 2420 | LyondellBasell Industries | Polyolefin, Unspecified | SEQUEL® |