Elastollan® C 65 A HPM
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SFBGDo_Elastollan-C-65-A-HPM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, very good damping and resilience performance, heat resistance and improved cycle times. Typical applications (Automotive) e.g. sealings, stop dampers, cable jackets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 67 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 55.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 20% Strain | 1.50 | MPa | |
| 100% Strain | 2.00 | MPa | |
| 300% Strain | 4.00 | MPa | |
| Tensile Stress | DIN 53504 | ||
| Yield 1 | 25.0 | MPa | |
| Yield | 37.0 | MPa | |
| Tensile Elongation | DIN 53504 | ||
| Break 2 | 900 | % | |
| Break | 950 | % | |
| Tear Strength 3 | 44 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 37 | % | |
| 100°C, 24 hr | 55 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVALAC RX®831 | Vyncolit N.V. | Phenolic | NOVALAC |
| DINALON® B1S25 M (Black) | Grupo Repol | Nylon 6 | DINALON® |
| FRblend® PP-1306 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | FRblend® |
| Hostacom G2 R03 105555 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| NORYL™ HNA055 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |