LNP™ THERMOCOMP™ AF004AHP compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SEQ9as_LNP-THERMOCOMP-AF004AHP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* AF004AHP is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this grade is: Healthcare. Also known as: LNP* THERMOCOMP* Compound AF-1004 HC Product reorder name: AF004AHP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 | % | |
| Across Flow : 24 hr | 0.55 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6250 | MPa | ASTM D638 |
| -- | 5960 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 69.0 | MPa | ASTM D638 |
| Break | 66.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 5860 | MPa | ASTM D790 |
| -- 5 | 5530 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 98.8 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 101 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 8 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D4812 |
| 23°C 9 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.9 | J | ASTM D3763 |
| -- | 2.48 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 104 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 99.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B27 E 01 | BASF Corporation | Nylon 6 | Ultramid® |
| Xuchuan 1001A/B-5301 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| NORYL™ PKN4752F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Electrafil® J-1/CF/10/TF/13/SI/2 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Hifax DRS723X | LyondellBasell Industries | TPO (POE) | Hifax |