DOW™ Butene 1211P
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ Butene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SENc6n_DOW-Butene-1211P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyethylene 1211P is a butene Linear Low Density Polyethylene for general blown film applications. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 8.19 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 183 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 217 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 10.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 31.7 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 660 | % | ASTM D882 |
| TD : Fracture, 51 µm | 710 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 110 | g | ASTM D1922 |
| TD : 51 µm | 260 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 101 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 116 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.8 µm) | 69 | ASTM D2457 | |
| Haze (50.8 µm) | 11 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Melt Temperature: 440°F (227°C) Die Gap: 70mil (1.8mm) Output: 120 lb/hr (55 Kg/hr) Blow Up Ratio: 2.5:1 Frost Line Height: 28 in. (71 cm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® C3 1 black (4546) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| Axiall PVC 12840 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina CLEAR PVC COMPOUND -E 70/206-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Rnew® B522 | Altuglas International of Arkema Inc. | PLA+PMMA | Plexiglas® |
| Infino GM-1080 | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |