TAROMID A 280 R3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SEB5BU_TAROMID-A-280-R3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 elastomer modified, very high impact resistance, low moisture absorption, very good chemical resistance to oils, solvents and other chemical substances. Available: different colors, UV-stabilized (L), release agent (W). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 to 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/1.0 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.3 to 1.8 | % | |
| Across Flow | 1.2 to 1.8 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.75 | % | ASTM D570, ISO 62 |
| Saturation | 5.5 | % | ASTM D570 |
| Saturation, 23°C | 5.5 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 80 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2050 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 85.0 | MPa | ISO 178 |
| Yield | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 180 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50, ASTM D1525 2 |
| Melting Temperature | 258 | °C | ASTM D211, ISO 121 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1600 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Sinvicomp SRF3711 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| ACCUTECH™ HP0336T30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Delrin® 510GR NC000 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Hostacom TRC 411N R C13034 | LyondellBasell Industries | PP, Unspecified | Hostacom |