LNP™ LUBRILOY™ D2000 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SDNHQZ_LNPLUBRILOYD2000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D2000 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound D Product reorder name: D2000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.70 - 0.90 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.70 - 0.90 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1860 | MPa | ASTM D638 |
| -- | 2150 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.7 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2 |
| Fracture | 60.2 | MPa | ASTM D638 |
| Fracture | 54.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.5 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2 |
| Fracture | 130 | % | ASTM D638 |
| Fracture | 99 | % | ISO 527-2 |
| Flexural Modulus | 2140 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 82.5 | MPa | ASTM D790 |
| -- | 78.5 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.16 | ASTM D3702 Modified | |
| With Self-Static | 0.090 | ASTM D3702 Modified | |
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D256 |
| 23°C 2 | 57 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 40.1 | J | ASTM D3763 |
| -- | 48.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 127 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 126 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 299 - 310 | °C | |
| Front Temperature | 304 - 316 | °C | |
| Processing (Melt) Temp | 304 - 316 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baoding 67I98 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Cheng Yu T881 | Cheng Yu Plastic Company Limited | PBT | Cheng Yu |
| Geon™ Vinyl Rigid Extrusion L0659 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| OmniCarb™ PC/PBT 1214 | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |
| Sylvin 4200-88UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |