Ultramid® A3K Q601
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SCioAV_Ultramid-A3K-Q601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3K Q601 is an easy flowing, injection molding grade PA66. Applications Typical applications include fast processing high stress technical parts or electrically insulating parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 83.0 | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2800 | 1100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 5.7 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength (23°C) | 5.2 | 14 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.750 mm | 80.0 | -- | °C | |
| 1.50 mm | 80.0 | -- | °C | |
| 3.00 mm | 80.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.400 mm | 65.0 | -- | °C | |
| 0.750 mm | 80.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 90.0 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-2 | -- | ||
| 0.750 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R210A80UV | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyether | Ravathane |
| TOTAL Polypropylene PPR 7238 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| APICAL 100AVY | Kaneka North America LLC | Film, PI | APICAL |
| IROGRAN® A 92 E 4738 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LNP™ COLORCOMP™ HF1130C compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |