OP - PPO PPOX-225-FR
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SChHYC_OP---PPO-PPOX-225-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP-PPO PPOX-225-FR is a polyphenylene ether PS (PPE PS) material,. This product is available in North America and is processed by injection molding. The main features of the OP-PPO PPOX-225-FR are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 53.1 | MPa | ASTM D638 |
| Fracture | 55.2 | MPa | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 270 | J/m | ASTM D256 |
| Dart Drop Impact | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 107 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 102 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | UL 94 | |
| 3.18 mm | V-0 | UL 94 |
| Additional Information |
|---|
| Melt Mass -Flow Rate (MFR), ASTM D1238, 315°C/ 5.0kg: 15 to 25 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 98.9 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 227 - 277 | °C | |
| Middle Temperature | 238 - 282 | °C | |
| Front Temperature | 249 - 288 | °C | |
| Processing (Melt) Temp | 260 - 288 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3463 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 300 GB 10 TFE 13 SI 2 | RTP Company | PC | RTP |
| Silplus® 80 MP | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Chiao Fu PA66 MD212STG18 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Sylvin 5196-90FU Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |