AIE PC 10G6F
| Category: | PC , Polycarbonate |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | AIE PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SCTg3R_AIE-PC-10G6F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AIE PC 10G6F is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of AIE PC 10G6F are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 2.2 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.40 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7400 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 19 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 143 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 110 to 130 | °C | |
| Injection Pressure | 40.0 to 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4210G50 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Nycal鈩?1850MC40 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Dynaflex™ G7660-1 (Natural) | PolyOne Corporation | TPE | Dynaflex™ |
| Karina WHITE PVC COMPOUND 750-10/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HI-ZEX MILLION™ 240M | Mitsui Chemicals, Inc. | HMWPE | HI-ZEX MILLION™ |