| BC 8163 is a very low viscosity, rapid setting, rigid urethane compound. This system will cure quickly to a hard, tough, impact resistant casting. BC 8163 is non-sensitive to moisture after cure and will readily bond to itself if stage pours are required. The one-to-one volume mix ratio makes the system readily adaptable for machine mixing and dispensing. BC 8163 is recommended in applications where a "thermoplastic feel" is desired. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.29 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 38.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 15200 | MPa | ASTM D790 |
| Flexural Strength (Break) | 54.3 | MPa | ASTM D790 |
| Compressive Strength | 27.5 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 57.2 | °C | ASTM D648 |
| CLTE - Flow | 2.4E-4 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 96, Mix Ratio by Volume: 100 | ||
| Resin | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Pot Life (25°C) | 2.0 to 2.5 | min | |
| Thermoset Mix Viscosity | 150 | cP | ASTM D2393 |
| Demold Time (25°C) | 60 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 GB 20 FR L | RTP Company | PC | RTP |
| Evermore PUR SA-2260L | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Diakon® CMG314V | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| KOPELEN JH-350 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Karina YELLOW COLOR CONCENTRATE -E 02/349-RG-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |