Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Osterman & Company
Trademark:	Osterlene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SB7S19_OsterleneLLSH0917SAH.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LLSH0917 is a super strength hexene copolymer LLDPE film resin. This product has outstanding toughness properties, especially impact and tear strength, compared to other hexene polymers. It is stabilized for blown film extrusion and does not contain slip or antiblock, making it well suited for blown stretch wrap.

Osterlene LLSH0917 meets the requirements of the Food and Drug Administration, 21 CFR Section 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations may apply. Contact your Osterman sales representative for more information.

General Information
Additive	Anti-caking agent slip agent
Features	High strength Copolymer hexene comonomer Impact resistance, good Good tear strength Good toughness Compliance of Food Exposure
Uses	Stretch winding
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Blow molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.917	g/cm³	Internal method
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.90	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Puncture Energy	3.62	J	Internal method
Film Puncture Force	44.5	N	Internal method
secant modulus			ASTM D882
1% secant, MD	165	MPa	ASTM D882
1% secant, TD	186	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield	8.96	MPa	ASTM D882
TD : Yield	9.65	MPa	ASTM D882
MD : Fracture	62.7	MPa	ASTM D882
TD : Fracture	51.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	630	%	ASTM D882
TD : Fracture	720	%	ASTM D882
Dart Drop Impact	330	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD	460	g	ASTM D1922
TD	600	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	125	°C	Internal method

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	37		ASTM D2457
Haze	17	%	ASTM D1003

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU P890	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
Telcar® TELC 3050	Teknor Apex Company	TPE	Telcar®
Clear Cote™ Clear Casting Resin	Club Kit, Inc.	Polyester, TP	Clear Cote™
Flontech® FT-STST50-1	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
GAPEX® RPP30EU55HB BLACK	Ferro Corporation	PP Copolymer	GAPEX®