Hanwha Total PP TF430
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SAc6KA_Hanwha-Total-PP-TF430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TF430 is a polypropylene terpolymer with ethylene and 1-butene comonomer. TF430 is used as a aluminium metallized layer for CPP(cast PP) film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 73 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 27.5 | MPa | |
| Break | 34.3 | MPa | |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 883 | MPa | ASTM D790 |
| Coefficient of Friction | 0.70 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - MD 4 | ASTM D882 | ||
| Yield | 24.5 | MPa | |
| Break | 39.2 | MPa | |
| Tensile Elongation - MD 5(Break) | 450 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 6 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 86 | ASTM D2457 | |
| Haze (30.0 µm) | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 300 mm/min |
| 5 . | 300 mm/min |
| 6 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN QHCA-352S | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| SilTRUST® TSE3661 | Momentive Performance Materials Inc. | Silicone | SilTRUST® |
| LEXAN™ VR2020 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LG PMMA HI855HS | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Sylvin 4200-88 Orange 5104 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |