Innothane® IE-3077
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SAEOle_Innothane-IE-3077.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3077 is a rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. IE-3077 has a very low mixed viscosity. It is ideal for color-matching due to its neutral semi-transparent appearance. Contact your Innovative representative to find out more about custom color-matching services. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.03 | g/cm³ | |
| Cured | 1.08 | g/cm³ | |
| Base Resin | 1.10 | g/cm³ | |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1840 | MPa | ASTM D790 |
| Flexural Strength | 64.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 60.0 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 94 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 20 to 40 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.040 | Pa·s | |
| 25°C 2 | 0.10 | Pa·s | |
| 25°C 3 | 0.25 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 4.0 to 6.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 80 | ASTM D2240 | |
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation at Break | 10 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH PZ780 | Polyram Ram-On Industries | PC | RAMTOUGH |
| BESTPOM C27/01 | Triesa Plastics | Acetal (POM) Copolymer | BESTPOM |
| Clyrell RC6034 | HMC Polymers | PP Terpolymer | Clyrell |
| DESLON™ 6 DSC101IG6 | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| Hostacom NXO21001 | LyondellBasell Industries | PP Copolymer | Hostacom |