Ecomann® Bioresin EM20010
| Category: | PHA , Polyhydroxyalkanoate |
| Manufacturer: | Shenzhen Ecomann Biotechnology Co., Ltd. |
| Trademark: | Ecomann® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S9qqLF_Ecomann-Bioresin-EM20010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EM20010 is semi-crystalline biodegradable, aliphatic bio-polyester designed for use in injection molding applications. EM20010 is PHA base compound with PLA, minerals and some additives. EM20010 is certificated to meet EN13432 & ASTM D6400 standards for biodegradable plastics. Typical applications: Personal care and cosmetic items, trays, disposable and single use items, caps and many other injection molding products |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Flexural Strength | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (Area) | 4.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 1 |
| Melting Temperature | 140 to 160 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 45 | YI | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 135 to 145 | °C | |
| Middle Temperature | 140 to 165 | °C | |
| Front Temperature | 140 to 175 | °C | |
| Nozzle Temperature | 140 to 165 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® PVDF FM 4910 | SIMONA AMERICA, Inc. | PVDF | SIMONA® |
| COSMOTHENE® F702-3 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| Elastollan® C 75 A HPM | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| KOPLA PC KBP1100 | KOPLA Co., Ltd. | PBT | KOPLA PC |
| Kinta NI6000 | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |