Zhongfa PC FR2840G
| Category: | PC , Polycarbonate |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S9eIO7_Zhongfa-PC-FR2840G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PC FR2840G is a polycarbonate (PC) material, which contains a 40% glass fiber reinforced material. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Zhongfa PC FR2840G are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.20 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 158 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 9600 | MPa | ASTM D790 |
| Flexural Strength | 186 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 154 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 13 kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 210 - 255 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 70.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 21Z-NT01A2 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| TYNEA 900 | Tyne Plastics LLC. | Acetal (POM) Copolymer | TYNEA |
| Electrafil® HDPE 1000 | Techmer Engineered Solutions | HDPE | Electrafil® |
| Geon™ Vinyl Wire & Cable W780L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Deprene 251-60 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |