RTP 2205 TFE 15
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S8yuSt_RTP-2205-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. PEEK is a high performance crystalline thermoplastic combining the chemical and thermal properties of some thermosets and ease of processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.011 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 145 | MPa | ASTM D638 |
| -- | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 234 | MPa | ASTM D790 |
| Yield | 234 | MPa | ASTM D790 |
| Coefficient of Friction (With Metal-Dynamic) | 0.20 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, RTP Tested) | V-0 | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, ASTM D955, 0.25in: 3 mil/inWear Factor, K, ASTM D-3702: 75E-10in³/min/ft/lb/hrThe coefficient of friction was tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 357 - 427 | °C | |
| Middle Temperature | 357 - 427 | °C | |
| Front Temperature | 357 - 427 | °C | |
| Mold Temperature | 121 - 204 | °C | |
| Injection Pressure | 82.7 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHE7000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Unichem 4543 | Colorite Polymers | PVC, Flexible | Unichem |
| Evolue™ SP1521 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Petrotene® PP A3 G45 NTLA010 PH367 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| HIPEX® HX7IDN (Series: HTR/OR) | KRAIBURG TPE | TPE | HIPEX® |