Durethan® B 30 S 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S8uUE9_Durethan-B-30-S-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, injection molding |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.14 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.14 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ||||
| Across Flow : 260°C, 3.00 mm 1 | 1.2 | -- | % | ISO 2577 |
| Across Flow : 120°C, 2 hr, 3.00 mm 2 | 0.40 | -- | % | ISO 294-4 |
| Flow : 260°C, 3.00 mm 3 | 1.0 | -- | % | ISO 2577 |
| Flow : 120°C, 2 hr, 3.00 mm 4 | 0.32 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 140 | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 3200 | 1100 | MPa | ASTM D638 |
| -5°C | 3200 | 1000 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Yield, 23°C | 80.0 | 40.0 | MPa | ASTM D638, ISO 527-2/50 |
| Break, 23°C | 50.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 20 | % | ASTM D638, ISO 527-2/50 |
| Break, 23°C | 35 | > 50 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 20 | > 50 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 800 | MPa | |
| 1000 hr | -- | 600 | MPa | |
| Flexural Modulus | ||||
| 23°C | 2700 | 703 | MPa | ASTM D790 |
| 23°C 6 | 2900 | 850 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 5.0% Strain, 23°C | 115 | 35.0 | MPa | ASTM D790 |
| 3.5% Strain 7 | 95.0 | 25.0 | MPa | ISO 178/A |
| 23°C 8 | 110 | 35.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 9(23°C) | 6.0 | 8.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 10(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GR, 14-030 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 11 | 10.0 | -- | J | |
| -- 12 | 12.0 | -- | J | |
| Film Puncture Force | ISO 6603-2 | |||
| -- 13 | 6540 | -- | N | |
| -- 14 | 5140 | -- | N |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact | ||||
| 23°C, 3.18 mm | 59 | 750 | J/m | ASTM D256 |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed, 3.99 mm | 180 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.99 mm | 60.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 45.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 15 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.1E-4 | -- | cm/cm/°C | |
| RTI Elec (1.50 mm) | 105 | -- | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | -- | °C | UL 746 |
| RTI Str (1.50 mm) | 75.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 to 1.0E+14 | 1.0E+12 to 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 30 | 30 | kV/mm | |
| 23°C, 3.00 mm | 30 | 35 | kV/mm | |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 16 | 3.80 | 20.0 | ||
| 23°C, 1 MHz 17 | 3.40 | 4.60 | ||
| 23°C, 100 Hz | 4.00 | 15.0 | ||
| 23°C, 1 MHz | 3.50 | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.050 | 2.3 | ||
| 23°C, 100 Hz | 0.017 | 0.20 | ||
| 23°C, 1 MHz | 0.020 0.070 | 0.12 0.40 | ||
| Comparative Tracking Index | ||||
| Solution A 18 | 600 | -- | V | IEC 60112 |
| Solution B | 600 | -- | V | IEC 60112 |
| -- | -- | 600 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 19 | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 500 Bar |
| 2 . | 150x150x3 |
| 3 . | 150x150x3; MT 80°C; 500 Bar |
| 4 . | 150x150x3 |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Pull Rate: 2 mm/min; 50% RH |
| 10 . | US-FMVSS302 |
| 11 . | -30°C |
| 12 . | 23°C |
| 13 . | -30°C |
| 14 . | 23°C |
| 15 . | 10°C/min |
| 16 . | Tinfoil Electrodes |
| 17 . | Tinfoil Electrodes |
| 18 . | Depth of Erosion: 1.30 mm |
| 19 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene CPP1040 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| BMC T15(F) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Braskem PE LBH 0120 BPS | Braskem | LLDPE | Braskem PE |
| Luxus PP 16192 | Luxus Limited | PP, Unspecified | Luxus PP |
| LNP™ LUBRICOMP™ Lexan_LF1530A compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |