TECHNYL® A 216 V33 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S7tgNR_TECHNYL-A-216-V33-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 216 V33 Natural is a polyamide 66, reinforced with 33% of glass fibre, for injection moulding. This product is available in natural color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.78 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.620 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 7900 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 195 | 135 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.6 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 8800 | 6200 | MPa | ISO 178 |
| Flexural Stress | 290 | 190 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 89 | 96 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 12 | 17 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 95 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | -- | °C | ISO 75-2/Af |
| Peak Melting Temperature | > 255 | -- | °C | ASTM D3418 |
| CLTE - Flow (23 to 85°C) | 2.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 2.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.75 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 500 | 500 | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.60 mm | 650 | -- | °C | |
| 3.20 mm | 750 | -- | °C | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 HV 0 H FR | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Technacet® B-110 | Poly Plastic | Acetal (POM) Homopolymer | Technacet® |
| Sylvin 9726-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Advanced Composites BJ4H-CS BDX | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| LNP鈩?THERMOCOMP鈩?PX85100 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |