Latigea B01 I6
| Category: | PLA , Polylactic Acid |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigea |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S7iuSK_Latigea-B01-I6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bio-Polymer (PLA, PHB, ...). Unfilled. Good elongation. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.25 to 0.65 | % | |
| Flow : 2.00 mm | 0.20 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 55.0 | MPa | |
| Break, 23°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 2.2 | % | |
| Break, 23°C | 90 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 50.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 55.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 to 50.0 | °C | |
| Drying Time | 6.0 | hr | |
| Processing (Melt) Temp | 170 to 190 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2700-50A | RTP Company | SEBS | RTP |
| Tritan™ MX810 | Eastman Chemical Company | Copolyester | Tritan™ |
| Karina IVORY PVC COMPOUND 750-35/1-B-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| MAJORIS FD905U | AD majoris | PP, Unspecified | MAJORIS |