ADVANCENE™ EM-5204-UVH

Category:	HDPE , High Density Polyethylene
Manufacturer:	ETHYDCO
Trademark:	ADVANCENE™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	S7Hp59_ADVANCENEEM5204UVH.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ADVANCENE™ EM-5204-UVH High Density Polyethylene (HDPE) Resin is produced via advanced gas phase PE process and is intended for use in injection molding applications such as caps & closures, pails, industrial parts and other shipping containers. This resin has been designed to provide excellent processability for molders and to meet the rigorous performance characteristics of applications requiring stackability, environmental stress crack resistance and impact strength. This resin is also suitable for cast flm extrusion processing.

Main Characteristics:

For injection molded pails, industrial parts and other shipping containers.

For cast film extrusion.

Hexene High Density Resin.

Excellent impact strength, stress crack resistance and processability.

Very narrow molecular weight distribution.

General Information
Features	Excellent Processability High ESCR (Stress Cracking Resistance) High density hexene comonomer Impact resistance, high Narrow molecular weight distribution
Uses	Industrial components Shield cast film Barrel Shell Shipping container
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a European 2002/72/EC
Processing Method	cast film Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.952	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	4.4	g/10 min	ASTM D1238, ISO 1133
Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50)	22.0	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	59		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638, ISO 527-2
Yield	26.9	MPa	ASTM D638, ISO 527-2
Fracture	31.0	MPa	ASTM D638, ISO 527-2
Tensile Elongation			ASTM D638, ISO 527-2
Yield	9.0	%	ASTM D638, ISO 527-2
Fracture	1200	%	ASTM D638, ISO 527-2
Flexural Modulus - 2% Secant	1100	MPa	ASTM D790B, ISO 178

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength
-- ¹	84.1	kJ/m²	ASTM D1822
--	84.1	kJ/m²	ISO 8256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	72.0	°C	ASTM D648, ISO 75-2/B
Brittleness Temperature	< -76.0	°C	ASTM D746, ISO 974
Vicat Softening Temperature	129	°C	ASTM D1525, ISO 306
Peak Melting Temperature	131	°C	ASTM D3418, ISO 3146
Peak Crystallization Temperature (DSC)	119	°C	ASTM D3418, ISO 3146

Note Message
1 .	Type S

Resin Grade	Manufacturer	Category	Trademark
PRL PC-G20-(color)-1	Polymer Resources Ltd.	PC	PRL
Sinpolene HFR8124	Teknor Apex Asia Pacific PTE. LTD.	PP, Unspecified	Sinpolene
NORYL™ PX1390 resin	SABIC Innovative Plastics	PPE+PS	NORYL™
Clariant Nylon 6/6 PA-113G13	Clariant Corporation	Nylon 66	Clariant Nylon 6/6
Jampilen HP510M	Jam Polypropylene Company	PP Homopolymer	Jampilen