Stat-Tech™ ST7300-0005

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	PolyOne Corporation
Trademark:	Stat-Tech™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	S6bQeo_StatTechST73000005.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low-to-high levels of conductivity depending upon application requirements.

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 15% filler by weight
Features	Conductivity Electromagnetic shielding (EMI) Electrostatic discharge protection Radio frequency shielding (RFI)
Uses	Electrical/Electronic Applications Aerospace applications Parts under the hood of a car Business equipment Shell Printing machine parts
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.11	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.050 - 0.20	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	70.3	MPa	ASTM D638
Flexural Modulus	9650	MPa	ASTM D790
Flexural Strength	103	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm, Injection Molded)	53	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 3.18mm	100	°C	ASTM D648
1.8 MPa, unannealed, 3.18mm	95.0	°C	ASTM D648

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+2 - 5.0E+4	ohms	ASTM D257
Volume Resistivity	1.0E+2 - 5.0E+4	ohms·cm	ASTM D257

Injection	Nominal Value	Unit
Drying Temperature	80 - 85	°C
Drying Time	2.0	hr
Processing (Melt) Temp	221 - 249	°C
Mold Temperature	65 - 85	°C

Note Message
1 .	Type 1, 5.1 mm/min

Resin Grade	Manufacturer	Category	Trademark
SUMILITE® PVC VSS-F120-UV	Sumitomo Bakelite Co., Ltd.	PVC, Unspecified	SUMILITE® PVC
Cellophane™ 300P	Innovia Films Ltd.	Cellulose, Regenerated	Cellophane™
Comco PEEK GF 30	Comco-Plastic GmbH	PEEK	Comco
Karina IVORY PVC COMPOUND 751-35/ 1-F-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
VALOX™ 451E resin	SABIC Innovative Plastics	PBT	VALOX™