Miramid® VE15CW is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe for injection molding.

Important attributes of Miramid® VE15CW are:

Chemical Resistant

Crystalline

Fast Molding Cycle

Good Stiffness

Heat Resistant

Typical applications include:

Automotive

Engineering/Industrial Parts

Construction Applications

Electrical/Electronic Applications

Sporting Goods

General Information
Filler / Reinforcement	Glass Fiber, 15% Filler by Weight
Additive	Heat Stabilizer Mold Release
Features	Crystalline Fast Molding Cycle Fuel Resistant Good Flow Good Stability Good Stiffness Grease Resistant High Heat Resistance High Rigidity Oil Resistant Solvent Resistant
Uses	Automotive Applications Automotive Exterior Trim Building Materials Electrical/Electronic Applications Engineering Parts Machine/Mechanical Parts Sporting Goods
Forms	Granules
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1230	--	kg/m³	ISO 1183 ¹
Water Absorption				ISO 62 ²
Saturation	8.5	--	%
Equilibrium	2.0	--	%
Viscosity number	145	--	cm³/g	ISO 307, 1157, 1628 ³

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	5500	3200	MPa	ISO 527-2 ⁴
Tensile Stress (Break)	125	75.0	MPa	ISO 527-2 ⁵
Tensile Strain (Break)	3.0	11	%	ISO 527-2 ⁶
Flexural Modulus	190	100	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁷
-30°C	6.00	--	kJ/m²
23°C	7.00	11.0	kJ/m²
Charpy impact strength				ISO 179/1eU ⁸
-30°C	35.0	--	kJ/m²
23°C	45.0	100	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ISO 75-2 ⁹
0.45 MPa	210	--	°C
1.8 MPa	190	--	°C
Melting Temperature (DSC)	220	--	°C	ISO 3146

Electrical	Dry	Conditioned	Unit	Test Method
Volume resistivity	1.0E+13	1.0E+10	ohms·m	IEC 60093 ¹⁰
Dielectric Constant (1 MHz)	3.50	6.00		IEC 60250
Dissipation Factor (1 MHz)	0.020	0.25		IEC 60250 ¹¹
Comparative tracking index	500	--		IEC 60112 ¹²

Injection	Dry	Unit
Processing (Melt) Temp	260 to 280	°C
Mold Temperature	80.0 to 100	°C

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
Radilon® A HS 372 M NER	Radici Plastics	Nylon 66	Radilon®
AKROMID® B3 GF 50 black (4907)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
INSTRUC PA66IM	Infinity LTL Engineered Compounds	Nylon 66	INSTRUC
LONGLITE® PBT 3020-200X	CCP Group	PBT	LONGLITE® PBT
POLYabs HH0	Polykemi AB	ABS	POLYabs