CoolPoly® D5110
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S5mryl_CoolPoly-D5110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 90.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 14000 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 14 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| Specific Heat | 1100 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 2.0 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461.The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551.The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461.Thermal Diffusivity, ASTM E1461: 0.0126 cm²/secSurface Resistivity, ASTM D257: >2E14 ohmsVolume Resistivity, ASTM D257: >3E16 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 282 - 299 | °C | |
| Middle Temperature | 288 - 307 | °C | |
| Front Temperature | 293 - 321 | °C | |
| Nozzle Temperature | 293 - 332 | °C | |
| Processing (Melt) Temp | 293 - 332 | °C | |
| Mold Temperature | 135 - 175 | °C | |
| Injection Pressure | 60.0 - 165 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 105 | MPa | |
| Back Pressure | 0.200 - 0.500 | MPa | |
| Screw Speed | 75 - 180 | rpm | |
| Cushion | 5.00 - 13.0 | mm | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® LX550 | Zeon Corporation | Latex | Nipol® |
| 3M™ Dyneon™ TFM™ Modified PTFE TFR 1502 A | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Grivory® GVS-5H nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| LEXAN™ ML7681 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ THERMOTUF™ WF003I compound | SABIC Innovative Plastics | PBT | LNP™ THERMOTUF™ |