OMIKRON FMS 30 R NERO 808
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S5h7mx_OMIKRON-FMS-30-R-NERO-808.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OMIKRON FMS 30 R is a copolymer polypropylene filled with 10% of talc for injection moulding, high processability. It is available in black or coloured version. OMIKRON FMS 30 R is suitable for moulding of items requiring stiffness and dimensional stability well as good aesthetic. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| 0°C | 7.5 | kJ/m² | ISO 180 |
| 23°C | 14 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 55.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 - 260 | °C | |
| Middle Temperature | 210 - 260 | °C | |
| Front Temperature | 210 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.500 - 1.00 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7F-7015AUR | Spartech Polycom | PC | Spartech |
| THERMORUN® QT85MA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| APEX® 87-L252-C | Teknor Apex Company | PVC, Flexible | APEX® |
| DJSilicone NE-281 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Moplen EP332C | PolyMirae | PP Impact Copolymer | Moplen |