PRE-ELEC® TPU 1511
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S3S5Uk_PRE-ELEC-TPU-1511.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® TPU 1511 is electrically conductive polyester based thermoplastic polyurethane (TPU) compound. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® TPU 1511 has retained the excellent mechanical properties of the base elastomer. PRE-ELEC® TPU 1511 has been developed for extrusion but it can also be injection moulded. Typical applications included extruded conveyor belts, sheets and injection moulded technical parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 95 | ASTM D2240, ISO 868 | |
| Shaw D | 52 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 33.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 33.0 | MPa | ASTM D638 |
| 4.00 mm | 33.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 530 | % | ASTM D638, ISO 527-2 |
| Fracture | 560 | % | ASTM D638 |
| Fracture, 4.00mm | > 560 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 5.0E+2 | ohms·cm | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Injection Pressure: Low to Medium |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 210 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 210°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 700 SI 4 Z | RTP Company | HDPE | RTP |
| Tenite™ Propionate 350E0096912 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Keliren® CM3615 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Kepital® TE-33A | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Sylvin 9067-80 RED 604 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |