Ultramid® B3GM35 BKQ642 23220
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S3A6Vz_Ultramid-B3GM35-BKQ642-23220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade. Applications Typical applications include industrial articles requiring medium rigidity and high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation | 5.7 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | -- | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 130 | 65.0 | MPa | ASTM D638 |
| Break, 23°C | 130 | -- | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.7 | -- | % | ASTM D638, ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.9 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 40 | -- | J/m | |
| 23°C | 53 | 130 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 214 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 198 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LDPE XJ800 | Lotte Chemical Corporation | LDPE | SEETEC LDPE |
| StarTwist™ 315XT (transparent) | Innovia Films Ltd. | CA | StarTwist™ |
| LTM® 318-1B | Cytec Industries Inc. | Epoxy | LTM® |
| Petrothene® GA503027 | LyondellBasell Industries | LLDPE | Petrothene® |
| Sylvin 9604-90 Grey 9202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |