DAI-EL™ G-7452
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | DAI-EL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S32l8X_DAI-EL-G-7452.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DAI-EL G-7452 is a cure-incorporated copolymer with medium Mooney viscosity. It has excellent mold flow compared with fluoroelastomers of similar Mooney viscosity, making it well suited for compression, transfer or injection molding. DAI-EL G-7452 is designed for seals and other complex shapes, where higher elongation at molding temperatures provides easy part demolding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 42 | MU | |
| Fluorine Content | 66 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Temperature Brittleness - TR10 | -18 | °C | ASTM D1329 |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A 1 | 74 | ||
| Shore A 2 | 73 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% Strain, 25°C 3 | 4.50 | MPa | |
| 100% Strain, 25°C 4 | 4.70 | MPa | |
| Tensile Strength | |||
| Yield, 25°C 5 | 15.0 | MPa | |
| Yield, 25°C 6 | 15.3 | MPa | |
| Tensile Elongation | |||
| Break, 25°C 7 | 260 | % | |
| Break, 25°C 8 | 250 | % | |
| Compression Set | ASTM D395B | ||
| 200°C, 70 hr 9 | 15 | % | |
| 200°C, 70 hr 10 | 17 | % |
| Note Message | |
|---|---|
| 1 . | ODR, Strain: 3°, Test time: 12 min |
| 2 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 3 . | ODR, Strain: 3°, Test time: 12 min |
| 4 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 5 . | ODR, Strain: 3°, Test time: 12 min |
| 6 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 7 . | ODR, Strain: 3°, Test time: 12 min |
| 8 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 9 . | MDR 2000, Strain: 0.5°, Test time: 6 min |
| 10 . | ODR, Strain: 3°, Test time: 12 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEMICOSIL® 927 F | Wacker Chemie AG | Silicone | SEMICOSIL® |
| XANTAR® 24 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Formolene® E922 | Formosa Plastics Corporation, U.S.A. | HDPE, MMW | Formolene® |
| GLS Acetal VG59 | GLS Polymers Pvt. Ltd. | Acetal (POM) Copolymer | GLS Acetal |
| SABIC® PPcompound 15T1020 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |