LNP™ STAT-KON™ Lexan_LCF1506 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S2YwaQ_LNP-STAT-KON-Lexan-LCF1506-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON LEXAN_LC1500N compound is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.050 to 0.15 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.30 | % | |
| K (wear) Factor 1 | 1000 | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 2 | 10 | msec | FTMS 101B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 111 | MPa | |
| Break | 111 | MPa | |
| Tensile Elongation 4(Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 5 | 9080 | MPa | |
| 100 mm Span 6 | 8420 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Break, 50.0 mm Span 7 | 161 | MPa | |
| Break, 100 mm Span 8 | 154 | MPa | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.19 | ||
| vs. Steel - Static | 0.41 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 280 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 11.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 144 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 139 | °C | |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 277 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 288 to 316 | °C | |
| Nozzle Temperature | 288 to 316 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | 5000V to <50V |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 ICF 30 black (5119) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Dryflex® A1 600901 | ELASTO | SEBS | Dryflex® |
| Geon™ Vinyl Flexible MG23B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| G-Lex E52A003 | Gas Authority of India Limited | HDPE | G-Lex |
| Sylvin 3260-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |