| TRANSMARE® 35HNF30-0.001 is a 30% bamboo fiber reinforced polypropylene homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 9.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 3360 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00mm | 33.0 | MPa | ISO 527-2/50 |
| Fracture, 4.00mm | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00mm | 2.0 | % | ISO 527-2/50 |
| Fracture, 4.00mm | 2.1 | % | ISO 527-2/50 |
| Flexural Modulus | 3430 | MPa | ISO 178 |
| Flexural Stress | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 2.2 | kJ/m² | ISO 179/1A |
| 0°C | 2.4 | kJ/m² | ISO 179/1A |
| 23°C | 2.9 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 5.5 | kJ/m² | ISO 179/1U |
| 23°C | 7.8 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 2.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 8.1 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 138 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 180 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DuPure® SU 76 A | Ducor Petrochemicals BV | PP Impact Copolymer | DuPure® |
| Generic PP Copolymer - Unspecified | Generic | PP Copolymer | Generic |
| Karina GRAY PVC COMPOUND 751-18/369-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND -E 80/215-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MACOMASS PP MM-PP HE 81 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |