Multiuse Leostomer® LE-3160N
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Riken Technos Corp. |
| Trademark: | Multiuse Leostomer® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S2BooZ_Multiuse-Leostomer-LE-3160N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Multiuse Leostomer®LE-3160N is a thermoplastic polyurethane elastomer product,. It can be processed by extrusion and is available in North America or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 60 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.70 | MPa | ISO 37 |
| Tensile Stress (Yield) | 15.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 820 | % | ISO 37 |
| Tear Strength | 42 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| -- | 41 | % | ISO 815 |
| 70°C, 22 hr | 35 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (50°C, 24 hr, in IRM 902 oil) | -6.0 | % | ISO 1817 |
| Change in Tensile Strain at Break (50°C, 24 hr, in IRM 902 oil) | 13 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ISO 974 |
| Additional Information |
|---|
| The values listed above are tested in accordance with JIS K test methods.Rebound Resilience: 40% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Cylinder Zone 5 Temp. | 180 | °C | |
| Melt Temperature | 180 - 200 | °C | |
| Die Temperature | 190 | °C |
| Extrusion instructions |
|---|
| Screw L/D Ratio: 20.0:1.0Screw Speed: 10 to 40 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN QHCA-352M | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| RTP 300 L HF UV | RTP Company | PC | RTP |
| ALTECH® PA66 C 1000/671 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| APEX® 78-A447R-21 | Teknor Apex Company | PVC, Flexible | APEX® |
| KEBAFLEX® U A 85 EF B01 natural | BARLOG plastics GmbH | TPU, Unspecified | KEBAFLEX® |