SUPREME Specialty PS SP6630
| Category: | PS (Specialty) , Specialty Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S1ncYa_SUPREME-Specialty-PS-SP6630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUPREME Specialty PS SP6630 is a special polystyrene product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Europe or Asia Pacific. Typical application areas are: coating applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 2900 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 74.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257, 23°C, 3.2mm, injection molded: 1E11 to 1E12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | < 230 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fireguard® 910-LBF | Teknor Apex Company | PVC, Flexible | Fireguard® |
| Eastar™ 5011 | Eastman Chemical Company | Copolyester | Eastar™ |
| HiFill® PA6 IM 40 Z | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® 1302HP-10 | LG Chem Ltd. | PC | Lupoy® |