Stirofor® HI-V2 NATURALE
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Stirofor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S1CsNv_Stirofor-HI-V2-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hi-impact polystyrene, flame retardant grade |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 77.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 1 |
| Ball Pressure Test (75°C) | Pass | IEC 335 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Needle Flame Test | Pass | IEC 60695-11-5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 190 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R722 | Spartech Plastics | PMMA+PVC | Royalite |
| NORYL™ WCA871A resin | SABIC Innovative Plastics Asia Pacific | PPE | NORYL™ |
| AKROMID® A3 GF 30 S1 black (3723) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Chemical Resources HD07960 | Chemical Resources, Inc. | HDPE | Chemical Resources |
| Colorite 77 Series 7077 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |