Generic TPU-Polyester
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S15t56_Generic-TPU-Polyester.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPU-Polyester This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 - 1.23 | g/cm³ | ASTM D792 |
| 23°C | 1.15 - 1.25 | g/cm³ | ISO 1183 |
| -- | 1210 | kg/m³ | ISO 1183 1 |
| -- | 0.340 - 1.22 | g/cm³ | ASTM D1505 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 34.1 - 76.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.39 - 1.1 | % | ASTM D955 |
| Transverse flow : 23°C | 0.79 - 0.82 | % | ASTM D955 |
| 23°C | 0.76 - 0.82 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 - 0.40 | % | ASTM D570 |
| Solution Viscosity | 14850 - 35000 | mPa·s | ASTM D445 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 34 - 96 | ASTM D2240 | |
| 23°C | 30 - 98 | ISO 868 | |
| Shaw A, 3 sec | 80 - 98 | ISO 868 2 | |
| Shaw D, 15 sec | 32 - 60 | ISO 868 3 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 140 - 730 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 27.2 - 63.5 | MPa | ISO 527-2 |
| 23°C | 1.00 - 45.9 | MPa | ASTM D638 |
| 23°C | 0.500 - 22.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 10 - 740 | % | ASTM D638 |
| Fracture, 23°C | 320 - 940 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 13.4 - 403 | MPa | ASTM D790 |
| 23°C | 13.4 - 367 | MPa | ISO 178 |
| Taber Abrasion Resistance (23°C) | 8.80 - 71.2 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 20% strain, 23°C | 0.500 - 8.06 | MPa | ISO 37 |
| 50% strain, 23°C | 1.68 - 15.3 | MPa | ASTM D412 |
| 100% strain, 23°C | 1.62 - 19.1 | MPa | ASTM D412 |
| 100% strain, 23°C | 1.00 - 11.2 | MPa | ISO 37 |
| 300% strain, 23°C | 3.00 - 29.7 | MPa | ASTM D412 |
| 300% strain, 23°C | 1.50 - 35.2 | MPa | ISO 37 |
| Tensile Strength | |||
| Yield, 23°C | 23.7 - 55.7 | MPa | ASTM D412 |
| Yield, 23°C | 24.6 - 55.0 | MPa | ISO 37 |
| Fracture, 23°C | 23.7 - 64.1 | MPa | ASTM D412 |
| Fracture, 23°C | 19.0 - 55.0 | MPa | ISO 37 |
| 23°C | 25.0 - 40.3 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Yield | 390 - 800 | % | ASTM D412 |
| Fracture, 23°C | 340 - 750 | % | ASTM D412 |
| Fracture, 23°C | 300 - 950 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 33.3 - 206 | kN/m | ASTM D624 |
| Cracking | 34 | kN/m | ASTM D470 |
| 23°C | 32 - 190 | kN/m | ISO 34-1 |
| Compression Set | |||
| -- | 18 - 76 | % | ASTM D395 |
| 23°C | 19 - 30 | % | ISO 815 |
| Bayshore Resilience | 25 - 45 | % | ASTM D2632 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (23°C) | -29 - 7.0 | % | ASTM D471, ISO 1817 |
| Change in Volume (23°C) | 0.60 - 24 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -67.8 - -12.8 | °C | ASTM D746 |
| Glass Transition Temperature | |||
| -- | -50.0 - 0.00 | °C | ASTM E1356 |
| -- | -45.1 - -14.5 | °C | DSC |
| Vicat Softening Temperature | |||
| -- | 57.8 - 160 | °C | ASTM D1525 |
| -- | 38.9 - 155 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 68.0 - 215 | °C | |
| -- | 106 - 227 | °C | DSC |
| CLTE - Flow | 9.3E-5 - 2.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 2.5E+10 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 110 | °C | |
| Drying Time | 2.0 - 4.1 | hr | |
| Dew Point | -30.6 - -30.0 | °C | |
| Suggested Max Moisture | 0.069 - 0.070 | % | |
| Hopper Temperature | 29.4 - 33.1 | °C | |
| Rear Temperature | 184 - 201 | °C | |
| Middle Temperature | 184 - 211 | °C | |
| Front Temperature | 185 - 211 | °C | |
| Nozzle Temperature | 189 - 216 | °C | |
| Processing (Melt) Temp | 181 - 230 | °C | |
| Mold Temperature | 29.2 - 46.3 | °C | |
| Injection Pressure | 6.00 - 86.3 | MPa | |
| Holding Pressure | 3.00 - 4.23 | MPa | |
| Back Pressure | 0.165 - 0.834 | MPa | |
| Screw Speed | 49 - 130 | rpm | |
| Clamp Tonnage | 5.5 - 5.6 | kN/cm² |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU-PolyesterThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.3 - 107 | °C | |
| Drying Time | 1.5 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.070 | % | |
| Hopper Temperature | 32.5 - 36.2 | °C | |
| Cylinder Zone 1 Temp. | 172 - 179 | °C | |
| Cylinder Zone 2 Temp. | 177 - 185 | °C | |
| Cylinder Zone 3 Temp. | 177 - 193 | °C | |
| Cylinder Zone 4 Temp. | 176 - 201 | °C | |
| Cylinder Zone 5 Temp. | 169 - 183 | °C | |
| Adapter Temperature | 184 - 189 | °C | |
| Melt Temperature | 189 - 217 | °C | |
| Die Temperature | 186 - 191 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPU-PolyesterThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 NG1 GF 30 HLS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TOTAL Polypropylene PPR Z9450 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| AIE PP 80T4 | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |
| Braskem PP RP 350 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Kemcor MD 6530 | Qenos Pty Ltd | LMDPE | Kemcor |