HI-ZEX™ 5000SR
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | HI-ZEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RzHfGe_HI-ZEX-5000SR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HI-ZEX™ 5000SR is a High Density Polyethylene product. It can be processed by extrusion and is available in Asia Pacific, Europe, or North America. Applications of HI-ZEX™ 5000SR include adhesives/tapes and fabrics/fibers. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.37 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | 150 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 26.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | > 500 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ISO 306 |
| Melting Temperature | 132 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2720SN | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| Silopren® LSR 4020 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| SolVin 250SB | INOVYN | PVC, Rigid | SolVin |
| Latene® 7H2W-V0 | LATI S.p.A. | PP Homopolymer | Latene® |
| POCAN® BF 4409 000000 | LANXESS Corporation | PBT | POCAN® |