| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RzAVuH_DurethanBM240000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % mineral, injection molding, isotropic properties, low tendency to warp |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.46 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 3.00mm 1 | 1.2 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.20 | -- | % | ISO 2577 |
| Flow direction : 280°C, 3.00mm 3 | 1.3 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.17 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 205 | 85.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 5630 | 2140 | MPa | ASTM D638 |
| 23°C | 5800 | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 82.7 | 53.1 | MPa | ASTM D638 |
| Fracture, 23°C | 85.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break, 23°C) | 10 | 40 | % | ASTM D638, ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 5600 | 2000 | MPa | ASTM D790 |
| 23°C 5 | 5500 | 2000 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 150 | 64.8 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 145 | 60.0 | MPa | ISO 178/A |
| 23°C 6 | 150 | 65.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | 8.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, MHR, 14-060, MD40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 140 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 75 | 85 | kJ/m² | ISO 180/1U |
| 23°C | 100 kJ/m² | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 3.00 | -- | J | ISO 6603-2 |
| 23°C | 20.0 | 65.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 728 | -- | N | ISO 6603-2 |
| 23°C | 3030 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 500 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 500 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC PHS 75/B | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Ebalta Silicone High Solid | Ebalta Kunststoff GmbH | Silicone | Ebalta |
| HiFill® TPX-IONOMER-02045 BK | Techmer Engineered Solutions | Ionomer | HiFill® |
| Jampilen HP552J | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| POLYFLON™ F-205 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |