INSULCAST® 333/INSULCURE 9
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RyPDlS_INSULCAST-333-INSULCURE-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 333 is a moderate viscosity, self-extinguishing, epoxy potting/casting compound which conforms to the component program of Underwriters Laboratories' Flame Class 94V-O. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Strength | 121 | MPa | ASTM D790 |
| Compressive Strength | 96.5 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.62 | W/m/K | |
| Heat Deflection Temperature | 80 | °C | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.40 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 6.0 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | |||
| -- 3 | 0.968 | g/cm³ | |
| -- 4 | 1.55 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 5 | 0.055 | Pa·s | |
| -- 6 | 2.0 | Pa·s | |
| 25°C 7 | 13 | Pa·s | |
| Curing Time | |||
| 50°C | 2.0 | hr | |
| 25°C | 8.0 to 12 | hr | |
| Pot Life 8(25°C) | 60 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 9 |
| 2 . | INSULCAST 333 |
| 3 . | INSULCURE 9 |
| 4 . | INSULCAST 333 |
| 5 . | INSULCURE 9 |
| 6 . | Mixed |
| 7 . | INSULCAST 333 |
| 8 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP501M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Double Elephant SX-304 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| LEXAN™ HP1REU resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| PERLER® O07N0001B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| Polygen SC75D-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |