RTP 4603 HI

Category: SPS , Syndiotactic Polystyrene
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: RyL3gI_RTP-4603-HI.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Glass Fiber - Impact Modified
General Information
Filler / Reinforcement
  • Glass Fiber, 20% Filler by Weight
Additive
  • Impact Modifier
Features
  • Impact Modified
RoHS Compliance
  • Contact Manufacturer
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.15g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.40%ASTM D955
Water Absorption (23°C, 24 hr)0.010%ASTM D570
Moisture Content 0.020%
Additional InformationNominal ValueUnit
Primary Additive 20%
MechanicalNominal ValueUnitTest Method
Tensile Modulus 6210MPaASTM D638
Tensile Strength 86.2MPaASTM D638
Tensile Elongation (Yield)2.6%ASTM D638
Flexural Modulus 6210MPaASTM D790
Flexural Strength 131MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)130J/mASTM D256
Unnotched Izod Impact (3.20 mm)530J/mASTM D4812
InjectionNominal ValueUnit
Drying Temperature 82.2°C
Drying Time 2.0hr
Dew Point -28.9°C
Processing (Melt) Temp 293 to 327°C
Mold Temperature 71.1 to 149°C
Injection Pressure 68.9 to 103MPa
Resin Grade Manufacturer Category Trademark
RTP 103 CC HF RTP Company PP, Unspecified RTP
Taitacell EPS 321LF Taita Chemical Company, Ltd. PS (EPS) Taitacell
TOTAL Polyethylene HDPE 2285 TOTAL Refining & Chemicals HDPE, HMW TOTAL Polyethylene
K-Bin Rigid PVC KB-2000 K-Bin, Inc. PVC, Rigid K-Bin Rigid PVC
Lupolen 4021 K RM Black Powder LyondellBasell Industries MDPE Lupolen