LNP™ THERMOCOMP™ CF008 compound
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RxFvlg_LNPTHERMOCOMPCF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP CF008 is a compound based on Polystyrene resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound CF-1008 Product reorder name: CF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.60 | % | ASTM D638 |
| Flexural Modulus | 11200 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 120 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 88.9 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® D DX9321 | Evonik Industries AG | Nylon 612 | VESTAMID® D |
| Nylfor® B2 GF/50 NATURALE | SO.F.TER. SPA | Nylon 6 | Nylfor® |
| HiFill® HDPE GF25 CC | Techmer Engineered Solutions | HDPE | HiFill® |
| Hiprolon® 70 HVN | Arkema | Nylon 610 | Hiprolon® |
| POLYFLON™ M-392 | Daikin Fluorochemicals (China) Co., Ltd. | PTFE | POLYFLON™ |