VALOX™ 310SE0 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RwZLoY_VALOX310SE0resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.710 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/2.16 kg | 8.6 | g/10 min | ASTM D1238 |
| 265°C/5.0 kg | 33 | g/10 min | ASTM D1238 |
| 266°C/5.0 kg | 33 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| 250°C/5.0 kg | 15.0 | cm³/10min | ISO 1133 |
| 265°C/5.0 kg | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 1.1 - 1.8 | % | Internal method |
| Flow 2 | 0.90 - 1.6 | % | Internal method |
| Flow 3 | 1.5 - 2.3 | % | Internal method |
| Flow : 3.20mm | 1.5 - 2.3 | % | Internal method |
| Transverse flow 4 | 0.90 - 1.9 | % | Internal method |
| Transverse flow 5 | 1.0 - 1.7 | % | Internal method |
| Transverse flow 6 | 1.6 - 2.4 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.36 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 7 | 2700 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 8 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 9 | 40.0 | MPa | ASTM D638 |
| Fracture | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 10 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture 11 | 15 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 12 | 2620 | MPa | ASTM D790 |
| -- 13 | 2600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0mm span 14 | 101 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 19.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 15 | 4.0 | kJ/m² | ISO 179/1eA |
| -30°C | 5.0 | kJ/m² | ISO 179/2C |
| 23°C 16 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 17 | ISO 179/1eU, ISO 179/2U | ||
| -30°C | No Break | ISO 179/1eU, ISO 179/2U | |
| 23°C | No Break | ISO 179/1eU, ISO 179/2U | |
| Notched Izod Impact | |||
| -30°C | 40 | J/m | ASTM D256 |
| 0°C | 45 | J/m | ASTM D256 |
| 23°C | 45 | J/m | ASTM D256 |
| -30°C 18 | 5.0 | kJ/m² | ISO 180/1A |
| 0°C 19 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 20 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D4812, ISO 180/1U | ||
| -30°C | No Break | ASTM D4812, ISO 180/1U | |
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 200 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 160 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 162 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 21 | 160 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 71.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 22 | 60.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 23 | 75.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 170 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 24 |
| -- | 212 | °C | ASTM D1525, ISO 306/A50 16 25 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : 60 to 138°C | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 1.60 mm, in Oil | 26 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 18 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 18 | kV/mm | ASTM D149 |
| 0.800mm, in oil | 39 | kV/mm | IEC 60243-1 |
| 1.00 mm 26 | 18 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.00 | ASTM D150, IEC 60250 | |
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 100 Hz | 3.10 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.015 | ASTM D150 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 1.5E-3 | IEC 60250 | |
| Arc Resistance 27 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | IEC 60112 |
| Solution B | 100 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 6 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 260 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 238 - 254 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 48.9 - 76.7 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.013 - 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 0.75 to 2.3 mm |
| 3 . | 2.3 to 4.6 mm |
| 4 . | Tensile Bar |
| 5 . | 0.75 to 2.3 mm |
| 6 . | 2.3 to 4.6 mm |
| 7 . | 5.0 mm/min |
| 8 . | Type 1, 50mm/min |
| 9 . | Type 1, 50mm/min |
| 10 . | Type 1, 50mm/min |
| 11 . | Type 1, 50mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | 1.3 mm/min |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 sp=62mm |
| 17 . | 80*10*4 sp=62mm |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 120*10*4 mm |
| 22 . | 120*10*4 mm |
| 23 . | 80*10*4 mm |
| 24 . | 标准 B (120°C/h), 载荷2 (50N) |
| 25 . | 速率 A (50°C/h), 载荷2 (50N) |
| 26 . | Short-Time |
| 27 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V515TL20 | Lucent Polymers, Inc. | PP, Unspecified | Primefin |
| Telcar® TL-1522A | Teknor Apex Company | TPE | Telcar® |
| Clearflex® H&T LFH 208 | Versalis S.p.A. | LLDPE | Clearflex® H&T |
| Generic PP Impact Copolymer | Generic | PP Impact Copolymer | Generic |
| FUDOWLITE® F5750F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |