Sindustris POM HI511
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rw4prh_Sindustris-POM-HI511.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris POM HI511 is an Acetal (POM) Homopolymer material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris POM HI511 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.7 to 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 90 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 64.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 95.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 150 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.950 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 170 to 190 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.490 to 3.04 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 D MS 5 | RTP Company | Nylon 612 | RTP |
| TOTAL Polypropylene PPC 4944CWZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Chemraz SD625 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| Karina YELLOW PVC COMPOUND 550D02/101-AT-IS (MECESA) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Monprene® CP-19963 NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |