Moplen EP310D
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RvgRgp_Moplen-EP310D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP310D is a low fluidity heterophasic copolymer designed for extrusion applications where smooth processability and high mechanical properties are of the utmost importance. Main applications are extrusion of film for heavy duty applications, adhesive tapes, lamination film and extrusion blow moulded containers for e.g. detergents. Moplen EP310D is suitable for food contact. For regulatory information please refer to Moplen EP310D Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.95 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 26.0 | MPa | ISO 527-2/50 |
| Break | 30.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 13 | % | |
| Break | > 500 | % | |
| Flexural Modulus | 1050 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - MD (50 µm, Cast Film) | 500 | MPa | ASTM D882 |
| Tensile Strength - MD 1 | ASTM D882 | ||
| Yield, 50 µm, Cast Film | 16.0 | MPa | |
| Break, 50 µm, Cast Film | 63.0 | MPa | |
| Tensile Elongation - MD 2(Break, 50 µm, Cast Film) | 830 | % | ASTM D882 |
| Dart Drop Impact (Cast Film) | > 1500 | g | ASTM D1709 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 70 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (50.0 µm, Cast Film) | 17 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 48 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 887 | RTP Company | Acetal (POM) Copolymer | RTP |
| WMB 126M | Pooya Polymer Tehran | Polyolefin, Unspecified | WMB |
| Huafon HF-3695AT | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Karina GRAY PVC COMPOUND 802D18/441-CY-IS-AS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Monprene® MP-2465A | Teknor Apex Company | TPE | Monprene® |